Description
Suffix EP MHR 101 is 2 component transparent casting epoxy resin. Its crystal clear liquid and its designed to be used for filling hairline cracks in wood, as well as sealing wood before casting. Our product its also used to close gaps, cracks or defects in hard-to-reach areas for repair purposes. Apart from that, it is also used for lamination on various surfaces.
Areas of Use
filling hairline cracks in wood, sealing wood before casting, closing gaps, cracks or defects in hard-to-reach areas for repair purposes, lamination on various surfaces like wood, marble, other natural stone surfaces and etc.
Advantages
Its crystal clear, can be coloured with different pigments, its perfect for decorative repairs, it has low viscosity and can be used on all surfaces like wood, concrete and glass and etc.
Technical Properties
- Volume – 100%
- Viscosity – 300 – 500
- Density – 1070
- Hardness (Shore D) – 82
- Thermal Resistence – 75 °C
- Mixing Ratio – 100:25
- Curing Time – 12 hours
- Full Curing – 2 days
Preparation
To achieve perfect results, the mixing ration must be applied correctly. Changin the mixing ratio causes the surface ro not dry properly and not reach its full mechanical properties. Its essential to use scale while preparing the mixture.
The application surface must be solid. Ambient temperature should be 18-23 °C and humidity should be below 50%
Application
25g of component B must be mixed with 100g of component A by weight. When weighing, component B should be weighted first and then component A should be added to it. To obtain a homogeneus mixture, the components must be mixed thoroughly at low speed for 3-4 minutes. The system tends to heat up in the container it is mixed in. Only the amount of product needed to be applied should be mixed. The maximum mixing amount is 500g of the product.
Storing and Shelf Life
It should kept tightly at room temperature, protected from sunlight. The Resin should be at 22-25 °C. Keeping the epoxy at lower temperatures causes crystallization and in this case a clear mixture cannot be obtained. If the Epoxy Temperature is below 10 °C, the temperature of the material should be carefully increased to 22-25 °C with a water bath in the container
It can be stored in its unopened original containers for 1 year from the date of production. Material in opened buckets should be used immediately.
Consuption
(A+B) – 1m2 with 1mm tickness = 1.07 kg